Waspaloy UNS N07001 W.Nr.2.4654 Ni-Cr-Co Based Superalloy Wire Rod
|
Dettagli:
Termini di pagamento e spedizione:
|
Descrizione di prodotto dettagliata
| Composizione chimica: | Ni-Cr-Co | Applicazione: | N07001 |
|---|---|---|---|
| Forma: | asta | Dimensioni: | 1,0 mm |
| Colore: | Bianco argentato | Standard: | ASTM, ASTM ASME YB HB BJB GB |
Waspaloy is Ni-Cr-Co based superalloy.Excellent mechanical properties below 980 ° C (1800 ° F), high strength and oxidation resistance at 760-870 ° C (1400-1600 ° F).
Its strength is superior to that of alloy 718 at temperature above 1200-1300℉(650-750℃), and is generally comparable to Haynes R-41 alloy.
Waspaloy Material Composition
| C | Cr | Mo | Ni | Co | Al | Ti | Fe | Si | Mn | P | S | B | Zr | Cu |
| 0.03-0.1 | 18-21 | 3.5-5 | Balance | 12-15 | 1.2-1.6 | 2.75-3.25 | ≤2 | ≤0.15 | ≤0.1 | ≤0.015 | ≤0.015 | 0.003-0.01 | 0.02-0.08 | ≤0.1 |
Waspaloy Material Mechanical Properties
| Grade | Density | Melting Point | Mechanical Property | |||||
| Temperature | Tensile Strength | Yield Strength | Elogation min | Ψ min | Hardness min | |||
| Waspaloy | 8.22 |
1330-1360℃ 2426-2480℉ |
815℃ 1499℉ |
608 Mpa | / | 20 | 32 | 299-387 HBS |
Applications of Waspaloy
Gas Turbine Blades
Sealing Ring
Shaft
Turbine Disc
High Temperature Fasteners
Exotic Fasteners
Special Fasteners
| Alloy Name | Trade Name | UNS NO. | Germany Spec | French Spec | Specification |
| Waspaloy | / | N07001 | W.Nr.2.4654 | NC20K14 |
Waspaloy AMS5708 Waspaloy AMS5709 |
Waspaloy coefficient of thermal expansion
| θ/℃ | 20-100 | 20-200 | 20-300 | 20-400 | 20-500 | 20-600 | 20-700 | 20-800 | 20-900 |
| α | 12.47 | 12.73 | 13.04 | 13.53 | 13.97 | 14.47 | 15.05 | 15.68 | 15.95 |
Waspaloy thermal conductivity
| θ/℃ | 360 | 460 | 545 | 640 | 770 | 855 | 985 |
| W/(m·℃) | 16.8 | 18.3 | 20.2 | 22.4 | 24.1 | 25.3 | 28.0 |
Oxidation resistance in air with a duration of 100h
| θ/℃ | 900 | 1000 |
|
Oxidation rate g/(m2.h) |
0.083 | 0.226 |
Waspaloy welding
Can be fusion welded by argon-arc methods using a matched composition filler metal. If matching alloy is not available, then the nearest alloy richer in the essential chemistry (Ni, Co, Cr, Mo) shall be adopted.
Waspaloy machining
Heavy duty equipment and tooling shall be used to minimize work-hardening of it ahead of cutting.
Dettagli di contatto
Ohmalloy Material Co.,Ltd
Persona di contatto: Mr. Qiu
Telefono: +8613795230939
Invia la tua richiesta direttamente a noi
Più Cavo termico dello spruzzo
-
Filtro di alluminio a spruzzatura termica
-
Cavo termico dello spruzzo Zn85Al15
-
Cavi termico solido dello spruzzo Ni95Al5 rendimento elevato 2mm/di 1.6mm con l'iso/il CE
-
Resistenza della corrosione del cavo di Monel 400 di ripristino dell'elemento a macchina buona
-
Nimonic80A |UNS N07080 |Lega 80A | WS2.4952
-
Filo per saldatura Inconel 625 ERNiCrMo-3 con diametro di 1,0 mm per applicazioni resistenti alla corrosione e stabili ad alta temperatura